Product Name: 2A11 Aluminum Plate/Sheet
State: T4, T6, T351
Payment Terms: L/C, T/T, PayPal, Western Union
Product Indroduction2A11 aluminum alloy belongs to the AL-CU-MG series aluminum alloy, the main characteristics and application range: This is a high-strength hard aluminum, can be enhanced by heat treatment, in the quenching and quenching state of plastic medium,
Spot welding is good, with gas welding has a tendency to form intergranular cracks, and the machinability of alloy after quenching and cold hardening is still good.
1. Width:500mm-1500mm
2. Length: according to your requirements
3. CE & ISO
Product Data
Chemical Composition | ||||||||||
Alloy |
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Zn |
Ti |
Al |
Others |
Max |
Max |
Max |
Max |
Max |
Max |
Max |
Max |
Min | ||
2A11 |
0. 7 |
0. 7 |
3.8-4.8 |
0.4-0.8 |
0.4-0.8 |
0.3 |
0.15 |
The Remaining |
0.15 |
|
Mechanical Properties | ||||
Aluminum Alloy & Temper |
Tensile Strength Rm/Mpa |
Proof Strength Rp0.2/Mpa |
Percentage Elongation After Fracture A/% |
Hardness HB |
2A11-T4 |
≥425 |
≥275 |
12 |
120 |
2A11 is mainly used to produce various high load parts and components (but not including stamping parts forgings) such as aircraft skeleton parts, skin, bulkhead, wing ribs, wing beams, rivets and other 150 ℃ working parts.